Waterproof Strong Adhesion Construction Silicone Sealant For Dotted Glass panels
Features:
- Cures to form a unique, dry matt finish surface.
- Improved aesthetic performance; reduces long-term residue rundown on glass, metal panels or staining on porous substrates.
- Good working and tooling time.
- High modulus, high movement capability; can accommodate ±50% movement in a properly designed joint.
- Excellent weatherability; non-reverting silicone durability.
Application:
- For big glass panels, large aluminium plates, curtain walling etc.
- Expansion joints.
Benefits:
- Excellent weatherability, virtually unaffected by sunlight, rain, snow or ozone.
- Excellent unprimed adhesion to a wide variety of construction materials and building components.
- Ease of application – ready to use as supplied.
- Excellent rheology, low string upon gunning.
Color:
Black,White,Aluminum,Transparent, customizable
Packing:
- Cartridge 300ml/280ml, 1 x 24pcs per carton
- Sausage 600ml, 1 x 20pcs per carton
Use Restriction:
- 1.It can not be used as structual adhesive
- 2.Not suitable on the material which seep grease, plasticizing agent or solvent, such as the surface of oil-impregnated wood
- 3.It's not suitable on non-ventilated places, as silicone sealant requires absorbing moisture in air for curing
- 4.It's not suitable for continuous soggy places or wet places all the year round
- 5.It's not suitable for using when the temperature on the material surface is lower than 4℃ or higher than 40℃
Tranportation&Storage:
JS-208 is not a flammable and explosive material,so it can be transported as a normal non-hazardous product,it shall be stored in a dry,cool and well-ventilated plaoe below 27 degrees,as of production date,the storage period is 24 months.
Storage Condition:
- Under 27 ℃ cool dry and well ventilated place, avoid high temperature
- Shelf life: 12 month stored in cool and dry place. (+7 ℃-27 ℃)
Data Sheet:
| Density | 1.0±0.15 |
| Shelf time | 24 months |
| Appearance | Paste |
| Skin time | 8-12min |
| Curing time | ≤24hrs |
| Harness shore A | 20-30 |
| Tensile strength | ≥ 0.6Mpa |
| Ultimate elongation at break | ≥ 400 |
| Modulus 100 | 0.6 Mpa |
| Extrusion rate | 200-300 g/min |